ASTM A ASME SA “Standard Specification for Nickel and Nickel-Base Alloy-Clad Steel. Plate”. “STANDARD SPECIFICATION FOR NICKEL AND. Buy ASTM A SPECIFICATION FOR NICKEL AND NICKEL-BASE ALLOY-CLAD STEEL PLATE from SAI Global. Designation: A − 12Standard Specification for Nickel and Nickel-Base Alloy- Clad Steel Plate1 This standard is issued unde.
|Published (Last):||18 May 2017|
|PDF File Size:||11.48 Mb|
|ePub File Size:||16.74 Mb|
|Price:||Free* [*Free Regsitration Required]|
A — 09 Standard Speci? A number in parentheses indicates the year of last reapproval. This standard has been approved for use by agencies of the Department of Defense. The material is generally intended for pressure vessel use but may be used in other structural applications where corrosion resistance of the alloy is of prime importance.
The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. Current edition approved May 1, Originally approved in Last previous edition approved in as A — Such requirements may include, but are not limited to the following: Specify whether applicable to the cladding alloy, backing steel, or both atm Section If the requirements of this speci?
Materials and Manufacture 5. The base metal shall conform to the chemical requirements of the speci?
ASTM A265 Clad Plate
All asfm tensile test requirements of the speci? The properties thus determined shall meet all of the tensile test requirements for the base steel. The tensile properties thus determined shall meet the base steel requirements. The shear test, when speci? The minimum cladding thickness for shear testing shall be 0.
ASTM A265 GR 1 titanium alloy strip sheet plate
Testing for shear strength for clad plates with minimum cladding thickness of 0. These bend tests shall be made in the manner of the tension tests z265 in Fig. Greater separation shall be cause for rejection.
2a65 NOTE 2—Punch marks for measuring elongation after fracture shall be made on the? NOTE 3—The dimension t is the thickness of the test specimen as provided for in the applicable material speci? Number of Tests and Retests 8. Each specimen shall be in the? In reducing the thickness of the specimen, both the alloy 3 Metric Equivalents in. Permissible Variations Metric Equivalents in.
The reduced section shall have a gradual taper from the ends toward the center, with the ends 0. Gage Length cladding and the base steel shall be machined so as to maintain the same a2655 of clad metal to base steel as is maintained in the plate, except that the thickness of the clad material need not be reduced below 1? The sides of the bend test specimen used for bond strength determination may have the corners rounded to a radius not over 1? Chemical analysis may be accomplished by wet chemical or instrumental procedures.
If wet chemical procedures are used, millings may be taken only when the composite plate thickness is sufficient to permit obtaining millings without danger of contamination from the adjacent layer. If spectrometric procedures are used, the sample shall be exposed on the center line of the cladding when there is sufficient cladding a625 available so that there is no contamination from the adjacent base metal.
The material shall a2265 cleaned and sufficient millings taken to represent the full cross-section of the remainder.
ASTM A Clad Plate | ASTM A Plate | ASTM A Nickel Coated Plate
Workmanship Finish, and Appearance Asym purposes of de? Areas within 1 in. When none has been speci? Repair of Cladding by Welding Method of test and acceptance standard shall aastm as agreed upon between the purchaser and the manufacturer. The surface condition of the repaired area shall be restored to a condition similar to the rest of the cladding.
General Requirements for Delivery Reports shall include the results of ultrasonic inspection when Supplementary Requirement S12 is speci? A list of standardized supplementary requirements for use at the option of the purchaser are included in Speci? Several of those considered suitable for use with this speci? Other tests may be performed by agreement between the supplier and the purchaser.
Ultrasonic Examination in accordance with Speci? Approved May 1, ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned in this standard.
Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk of infringement of such rights, are entirely their own responsibility. This standard is subject to revision at any time by the responsible technical committee and must be reviewed every?
Your comments are invited either for revision of this standard or for astj standards and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of qstm responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should make your views known to the ASTM Committee on Standards, at the address shown below.
Individual reprints single or multiple copies of this standard may be obtained by contacting ASTM at the above address or at phonefaxor service astm.